Year: 2025
Type: article
Abstract: This study investigated the oxidative leaching of copper concentrate using a mixture of ferric ions and sulfuric acid solutions. We examined the effects of various parameters, including temperature, initial sulfuric acid concentration and slurry filtration conditions. At lower temperatures (150?C), the leaching process resulted in the elemental sulfur and jarosite minerals formed in the solid residue. In contrast, at higher temperatures (190?C), the solid residue contained jarosite and hematite, the most elemental sulfur-oxidizing to sulfuric acid. Under optimal conditions, a leaching temperature of 190?C, a concentrateto- leaching solvent (Fe3+ 5 g L-1 and H2SO4 50 g L-1) ratio of 1:8, an oxygen pressure of 1.0 MPa, and a solid phase particle size of less than 20 ?m the dissolution rate of copper reached 98 % after 3 h. When the sulfuric acid concentration increased from 30 to 100 g L-1, the amount of copper increased from 40 to 48 g L-1. Furthermore, rapid filtering of the leaching solution without cooling helped retain most of the iron in the solid phase, resulting in a relatively pure solution. The solid residue was analyzed using X-ray diffraction and scanning electron microscopy.
Institution: Mongolian University of Science and Technology
Language: English
Subfield: Biomedical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4412519381