Atomistic Thermodynamics of Water over Actinide Oxide Surfaces: Implications on Stabilities and Morphologies
Year: 2025
Type: article
Abstract: The surface free energy diagrams of water adsorption on the low-index surfaces of UO2 and PuO2 were calculated using the ab initio atomistic thermodynamics technique. The phase diagrams of both UO2(100) and PuO2(100) surfaces show that the dissociative H-OH adsorption of water exhibits higher stability for all applied coverages. Chemical potential, with PuO2(100) stabilizing hydroxylated structures at lower chemical potentials than UO2(100). On the (110) surfaces, dissociative adsorption is also preferred, but with reduced reactivity compared to (100); UO2(110) supports hydroxylation at lower chemical potentials than PuO2(110), indicating a greater tendency for early-stage protonation. On the closed-packed (111) surfaces, the stability diagrams revealed that only a mixed monolayer containing both molecular and dissociated water becomes stable, and only under more humid or elevated temperature conditions. The mixed adsorption phase on PuO2(111) becomes stable at a lower chemical potential relative to UO2(111), indicating slightly higher reactivity. The equilibrium morphology of UO2 and PuO2 nanoparticles in humid environments were predicted using the Wulff construction. The results showed that the (111) facets dominate across the full range of water chemical potentials, yielding octahedral nanoparticles. For PuO2, a transition to truncated octahedral was observed ∆𝜇𝐻2𝑂 = −0.50 eV due to the emergence of (110) facets. These findings clarify the role of thermodynamic and kinetic variables affecting water interactions with actinide oxides, pertinent to corrosion, catalysis, and the performance of nuclear materials.
Author: Niveen W. Assaf
Institution: Al-Balqa Applied University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4413019713