Combined Lithium-Rich Czochralski Growth and Diffusion Method for Z-Cut Near-Stoichiometric Lithium Niobate Crystals and the Study of Periodic Domain Structures

Year: 2025

Type: article

Abstract: This paper presents the preparation of Z-cut near-stoichiometric lithium niobate (NSLN) wafers using a combined process of the lithium-rich Czochralski growth and diffusion methods. The fabricated Z-cut NSLN wafers exhibited outstanding comprehensive performance, including a high Curie temperature of up to 1200 °C, a refractive index gradient in the diameter direction below 1.5 × 10−4 cm−1, and a UV absorption edge shifted 14 nm toward the ultraviolet region compared to congruent lithium niobate crystals, with a coercive field of 1268 V/mm. Additionally, the wafers demonstrated excellent processing characteristics, with the bow of 4-inch wafers controlled within 55 μm, surpassing the machining standards of traditional lithium niobate wafers of the same size. These results indicated the highly uniform chemical stoichiometry and crystallization quality of the wafers. Leveraging the high uniformity and low coercive field of the wafers, periodic triangular domain structure arrays were successfully fabricated, laying the foundation for domain engineering design in electro-optic deflectors and switching devices. This study not only achieves the scalable preparation of NSLN wafers but also provides a reliable technical solution for their practical applications in high-performance electro-optic devices.

Source: Crystals

DOI: 10.3390/cryst15080727