Effect of Foreign Object Damage on Corrosion Fatigue Behavior in Surface-Strengthened EA4T Railway Axle Steel

Year: 2025
Type: article
Abstract: The electrochemical behavior and corrosion fatigue property of the surface-strengthened EA4T axle steel subjected to foreign object damage (FOD) is investigated in this study. It is found that the corrosion resistance can be enhanced after being impacted by the foreign object due to the introduced hardening layer. Specifically, compared to the smoothed sample, the 167 m/s sample exhibited a 13.88% higher corrosion potential (Ecorr) and a 67.61% lower current density (icorr). The facture surface demonstrates that the corrosion pits on the surface are the main crack initiation location for the smoothed specimens. In contrast, for the surface-damaged specimens, cracks initiate around the crater. The foreign object impact speed has a significant influence on the corrosion fatigue strength; specifically, the faster the impact velocity, the greater the surface damage of the axle specimen, and the shorter its fatigue life at the same stress level. To address the combined influence of size effect and surface defects on fatigue performance, we constructed an improved Kitagawa–Takahashi (KT) diagram by incorporating the theoretical corrosion fatigue limit of full-scale axles with a surface damage of 270 MPa based on conditional probability density function (CPDF). Comparative analysis demonstrates that the revised KT diagram defines a narrower yet more conservative fatigue loading safety zone than the standard KT diagram. This refinement enhances reliability in practical applications where surface imperfections and scale effects dominate failure mechanisms.
Source: Technologies
DOI: 10.3390/technologies13080368
Authors: Yan Luo, Gang Li, Cunhai Li, Chuanqi Qi, Yongxu Hu, Ping Yuan
Language: English
Open Access status: gold
Estimated APC paid: $1,930
OpenAlex ID: W4413282818
FWCI:
Cites: 37
Cited by:
Related to: 10