Parameters Optimization for Manufacturing Advanced Self-Reinforced Composites based on Ultra-High Molecular Weight Polyethylene
Year: 2025
Type: article
Abstract: In this study, the relationships between processing, structure and properties of self-reinforced ultra-high molecular weight polyethylene (UHMWPE) composites fabricated via thermal pressing are investigated. By systematically varying processing temperatures (145, 155, 165, 170, 175,180 °C) and pressures (25 and 50 MPa), we demonstrate that mechanical performance is governed by the interplay between fiber consolidation and the preservation of the oriented crystalline phase. Scanning electron microscopy reveals the presence of residual voids that are independent of the processing parameters, and which lead to interfacial failure and fibrillar fracture morphologies. We identify a critical processing threshold at 165 °C (25 MPa), which yields peak interlayer shear strength (7.8–11.1 MPa), bending strength (102–130 MPa), elastic modulus (23–42 GPa), and Charpy impact resistance (72–95 kJ/m²). Beyond this threshold, however, mechanical performance deteriorates due to fiber remelting and loss of anisotropy, resulting in the composite transitioning to an isotropic UHMWPE matrix. Conversely, elevated pressures fail to improve properties due to insufficient macromolecular interdiffusion, which is the dominant bonding mechanism. These findings establish a processing-structure-property framework for UHMWPE-based self-reinforced composites that balances interfacial adhesion and crystalline alignment, while providing actionable guidelines for engineering high-performance single-polymer materials.
Institutions: National University of Science and Technology, Skolkovo Institute of Science and Technology, Sirius University of Science and Technology, Russian Academy of Sciences, Institute of Synthetic Polymeric Materials, Federal Service for Surveillance on Consumer Rights Protection and Human Wellbeing
Language: English
Subfield: Polymers and Plastics
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4413318242