Multi-step trap-assisted tunneling in Al-doped HfO2 used in advanced 2.5D metal–insulator–metal capacitors
Year: 2025
Type: article
Abstract: Leakage currents through back-end dielectric layers critically affect the performance and reliability of modern electronic devices. In particular, high-κ dielectrics, such as HfO2, used in backend-integrated decoupling capacitors, exhibit significant trap-assisted leakage currents. This study investigates the leakage of Al-doped HfO2 in advanced 2.5D metal–insulator–metal capacitors across a wide temperature range of 77–448 K. It was found that Fowler–Nordheim tunneling dominates at fields exceeding 5 MV/cm, while trap-assisted tunneling (TAT) governs the leakage in the intermediate field range. A multi-step TAT model, parameterized by the trap concentration and trap spacing of the dielectric, is employed to analyze the leakage behavior. The model successfully separates the dependence of the leakage current on the field, linked to the trap spacing, and on the temperature, attributed to an energy barrier for trap-to-trap tunneling. At higher temperatures, the conduction complies with a uniform trap distribution with a trap spacing of 3.52±0.16 nm and an energy barrier of 0.27±0.02 eV, in agreement with a measured trapped electron concentration of 3.1×1019 cm−3. As the temperature decreases toward 77 K, quantum mechanical tunneling becomes dominant, necessitating the presence of trap clusters. Our findings demonstrate that the leakage cannot be described by a single conduction mechanism over the entire temperature range; instead, the framework provides a more comprehensive understanding of the interplay between the field and temperature in governing the leakage behavior.
Source: Journal of Applied Physics
DOI: 10.1063/5.0277092
Authors: C. Fohn, E. Chery, K. Croes, M. Stucchi, V. Afanas’ev
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,500
OpenAlex ID: W4413380902