Dual-extended-polyhedral metal–organic frameworks for atmosphere water harvesting
Year: 2025
Type: article
Abstract: A series of dual-extended-polyhedral metal–organic frameworks (MOFs) are constructed based on the 14-coordinated Cu24-MOP-1 supermolecular building blocks (SBBs) with enhanced stability and tunable functionality for high water uptake efficiency and capacity. Exceptional water stability is demonstrated by the retention of chemical integrity and crystallinity of USC-CP-5 after exposure to boiling water for 24 hours. Functionalization with –Cl, –OCH3, –OH and –NH2 groups of USC-CP-5 resulted in water uptake capacities of 450, 460, 490, and 590 cm3∙g-1 at P/P0 = 0.9, respectively. This performance is ascribed to both, the increased hydrophilicity of the ligands and stronger hydrogen bonding. Intriguingly, high-temperature activated USC-5–NH2 exhibits a significant water uptake of 38.5 wt% at P/P0 = 0.3 and releases 0.44 L∙kg–1 water between 25 °C and 65 °C. This water release process is reversible for, at least, 100 cycles with minimal weight loss of only 1.6 wt%. Consequently, USC-5–NH2 holds considerable potential for harvesting and releasing atmospheric water in arid desert regions, powered by solar energy.
Source: Nano Research
Language: English
Subfield: Inorganic Chemistry
Field: Chemistry
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $5,290
OpenAlex ID: W4413435065