Judd–Ofelt-enhanced orange-red emission and dual-functional performance of NaBaBi2P3O12:Pr3+ phosphor for solid-state lighting and optical thermometry
Year: 2025
Type: article
Abstract: The pursuit of highly efficient red-emitting phosphors is essential for advancing solid-state lighting and optical sensing technologies. In this study, a novel series of Pr 3+ -doped NaBaBi 2 (PO 4 ) 3 phosphors was successfully synthesized using the conventional solid-state reaction method. Structural analysis using X-ray diffraction (XRD) confirmed the formation of a pure single-phase cubic structure; while scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) revealed the particle morphology and confirmed the elemental composition. Under 445 nm excitation, the phosphor exhibited an intense orange-red emission centered at 602 nm, with an optimal Pr 3+ doping concentration of 0.01 mol. Judd-Ofelt analysis yielded high intensity parameters, indicating strong electric dipole transitions and a favorable asymmetric coordination environment around the Pr 3+ ions. The photoluminescence lifetime measurements revealed microsecond-scale decay times, indicating efficient radiative recombination. Chromaticity analysis confirmed emission in the orange-red region, with CIE coordinates of (0.6333, 0.3663) and high color purity of 100 %. Thermal quenching studies demonstrated excellent thermal stability, with the phosphor retaining 75 % of its initial intensity at 423 K. Furthermore, a temperature-dependent decay analysis showed a systematic decrease in lifetime, attributed to thermally activated non-radiative transitions. The relative thermal sensitivity was determined to be 3 × 10 −2 %K −1 , underscoring its applicability in optical thermometry. These findings establish NaBaBi 2 (PO 4 ) 3 : Pr 3+ as a promising candidate for high-performance red phosphors in solid-state lighting and optical sensing systems.
Institution: Sri Sivasubramaniya Nadar College of Engineering
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,140
OpenAlex ID: W4413812089