Superconducting properties of YBCO/LaNiO 3 bilayers grown on (100) SrTiO 3 substrates

Year: 2025

Type: article

Abstract: High- T c superconducting YBa 2 Cu 3 O y / LaNiO 3 (YBCO/LNO) bilayers were grown by off axis magnetron sputtering on (100) SrTiO 3 substrates. Patterned samples with YBCO thicknesses of 50–100 nm and a fixed 20 nm LNO capping layer were measured with magnetic fields applied parallel to the c axis and within the ab plane. Relative to the well-studied single-layer YBCO, the bilayers exhibit a systematic suppression of superconductivity. Both the superconducting transition temperature ( T c ) and the thermally activated flux-flow activation energy ( U ) decrease with decreasing YBCO thickness. The scaling of U ( H ) together with the temperature dependence of H c 2 ( T ) near T c is consistent with quasi-two-dimensional (2D) superconductivity confined at the YBCO/LNO interface. We attribute this behavior to interfacial strain- and redox-driven oxygen redistribution during LNO deposition, possibly accompanied by limited Ni intermixing, which together create a nanometer-scale region of reduced dimensionality and lower T c . Interfacial superconductivity is established in oxide heterostructures and often shows quasi-2D behavior. Within this context, we present evidence consistent with quasi-2D behavior near T c and discuss an interface-driven scenario in cuprate–nickelate bilayers. Given theoretical proposals that LaNiO 3 heterostructures could host nontrivial band topology under suitable conditions, these results motivate further tests for possible topological superconductivity in this platform.

Source: Superconductor Science and Technology

DOI: 10.1088/1361-6668/ae01e8