Abstract: A group of renewable, unsaturated resins from itaconic acid, 1,8-octanediol, and succinic anhydride were synthesized in a non-solvent and non-catalyst melt polycondensation reaction. The study addresses the need for sustainable polymeric materials suitable for additive manufacturing by investigating the influence of synthesis parameters—namely itaconic acid content, reaction time, and temperature—on the properties of poly(octamethylene itaconate-co-succinate) (POItcSc). The Box-Behnken mathematical planning method was applied to optimize the reaction conditions. The optimal synthesis conditions of POItcSc were achieved with an itaconic acid molar fraction = 0.50:0.50, reaction time t = 7 h, and reaction temperature T = 150 °C. The conversion of the carboxyl group (by titration) was 83.3%, and the maintenance of C=C bonds (by NMR) was 88.7%. Structural characterization confirmed the formation of the desired polymer through FTIR and 1H NMR analyses. Molecular weight (Mn = 1001 g/mol for an optimal product), thermal behavior (DSC, TG, DTG), and rheological properties (η = 14.4 and 3.6 Pa∙s for an optimal product at 25 and 36.6 °C) were systematically evaluated. The synthesized POItcSc resins were transparent and exhibited physicochemical properties favorable for extrusion-based 3D printing techniques such as Direct Ink Writing, offering a promising alternative to conventional petrochemical-based inks.
Source: Polymers
Institution: Warsaw University of Technology
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,258
Awards: G5723133983, G6626388146
OpenAlex ID: W4413970271