Year: 2025
Type: article
Abstract: The ordered tetragonal FeNi L10 phase, tetrataenite, is a promising candidate for rare earth-free permanent magnets due to its competitive magnetic properties and the low cost of the constituent elements. In this work, we have investigated the effect of molybdenum and aluminum substitution on the formation of the ordered L10 phase. The alloys were prepared with die casting and melt spinning techniques, further processed using cold rolling and cryomilling, and finally annealed below the estimated order–disorder temperature (TOD). To study the influence of composition and processing of the alloys, structural characterization and microstructural analysis were performed with synchrotron radiation X-ray diffractometry (SR-PXD) and Scanning Transmission Electron Microscopy (STEM), respectively. The presence of tetrataenite in the alloys investigated in this work could not be confirmed. In situ SR-PXD and STEM indicated minimal structural changes in the temperature stability range of the materials. A full-loop hysteresis curve acquired using a vibrating sample magnetometer (VSM) indicated no signs of magnetic hardening of the alloys with the measured coercivity being below 10 Oe, and thus consistent with FeNi without ordering.
Source: Metals
DOI: 10.3390/met15090996
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4414141553