Abstract: The tribological behavior of ferritic ductile iron without ultrafine graphite nodules (FDI) and ferritic ductile iron with ultrafine graphite nodules (FDI-UG) was investigated in the present study. Ultrafine graphite nodules with a count of 3400 nod/mm2 were introduced by annealing treatment of quenched ductile iron, which effectively reduced the friction coefficient of ferritic ductile iron from approximately 0.3 to 0.15. This improvement was attributed to the ultrafine graphite nodules, which, due to their small spacing, facilitated a more uniform distribution on the tribological surface. Additionally, the formation of ultrafine graphite nodules in ferritized ductile iron refined the grain size (15 μm) and enhanced the hardness of ferritic ductile iron (183 HV), thereby significantly reducing abrasive wear. The more uniform graphite lubrication on the tribosurface and high hardness of fine ferrite grains in FDI-UG further enhanced wear resistance between the frictional pairs, effectively suppressing adhesion wear at high loads (6 N). Consequently, the ferritic ductile iron containing ultrafine graphite nodules and fine ferrite grains exhibited a superior wear resistance (6.84 × 10−3 mm3 and 9.47 × 10−3 mm3) compared to its untreated counterpart (9.22 × 10−3 mm3 and 11.95 × 10−3 mm3). These findings suggest that the incorporation of ultrafine graphite nodules was an effective strategy to enhance the tribological properties of ductile iron.
Source: Lubricants
Institution: Xi'an University of Technology
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4414146002