Pinless Friction Stir Spot Welding of Pure Copper: Process, Microstructure, and Mechanical Properties
Year: 2025
Type: article
Abstract: Pure copper joints (PCJs) were fabricated using pinless friction stir spot welding (P-FSSW), a solid-state welding technique, to investigate the influence of plunge depth, rotational speed, and dwell time on PCJ performance. Thermal cycles under different welding parameters were recorded, while the microstructure at various locations within the welded zone was characterized using electron backscatter diffraction (EBSD). The microhardness and tensile–shear force (T-SF) of the PCJs were evaluated, and the fracture types together with fracture evolution were analyzed. The experimental results reveal that, under the combined effect of thermal cycles and mechanical stirring, subgrains in the welded zone transformed into recrystallized grains, whereas intense material flow contributed to an increased fraction of deformed grains. At the Hook region and the interface between the upper and lower sheets, grains were tightly bonded, resulting in effective metallurgical joining. Higher microhardness values were observed in the stir zone (SZ), whereas lower values appeared in the heat-affected zone beneath the interface. With increasing plunge depth, rotational speed, and dwell time, the T-SF of the PCJs first increased and then decreased, achieving a relatively high value at a plunge depth of 0.4 mm, a rotational speed of 1500 rpm, and a dwell time of 9 s. The fracture types of the PCJs were shear fracture and plug fracture, with the Hook region identified as the weakest zone.
Source: Crystals
Authors: Xu Zhang, Xiaole Ge, Igor Kolupaev, Zhuangzhuang Shan, Hongfeng Wang
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,534
Funder: Huangshan University
OpenAlex ID: W4414259459