Cost-Effective Fabrication of Silica–Silver Microspheres with Enhanced Conductivity for Electromagnetic Interference Shielding

Year: 2025

Type: article

Abstract: A green and cost-effective method was employed to efficiently synthesize conductive silica–silver (SiO2/PCPA/Ag) core–shell structured microspheres. The SiO2 microspheres were initially functionalized with poly(catechol-polyamine), followed by the in situ reduction of Ag ions to Ag nanoparticles on the surface of the SiO2 microspheres using an electroless plating process. Analysis using scanning electron microscopy confirmed the successful formation of a dense and uniform silver layer on the surface of the SiO2 microspheres. The valence state of the silver present on the surface of the SiO2 microspheres was determined to be zero through analyses conducted using an X-ray photoelectron spectrometer and X-ray diffractometer. Consequently, the SiO2/PCPA/Ag microspheres, upon initial preparation, demonstrated a notable conductivity of 1005 S/cm, which was further enhanced to 1612 S/cm following additional heat treatment aimed at rectifying defects within the silver layer. The resulting rubber composites displayed a low electrical resistivity of 5.4 × 10−3 Ω·cm and exhibited a significant electromagnetic interference (EMI) shielding effectiveness exceeding 100 dB against both X-band and Ku-band frequencies, suggesting promising potential for utilization as a material for conducting and EMI shielding purposes.

Source: Nanomaterials

DOI: 10.3390/nano15181433