Lubrication Mechanism and Establishment of a Three-Phase Lubrication Model for SCCO2-MQL Ultrasonic Vibration Milling of SiCp/Al Composites
Year: 2025
Type: article
Abstract: SiCp/Al composites (Silicon Carbide Particle-Reinforced Aluminum Matrix Composites), due to their light weight, high strength, and superior wear resistance, are extensively utilized in aerospace and other sectors; nonetheless, they are susceptible to tool wear and surface imperfections during machining, which negatively impact overall machining performance. Supercritical carbon dioxide minimal quantity lubrication (SCCO2-MQL) is an environmentally friendly and efficient lubrication method that significantly improves interfacial lubricity and thermal stability. Nonetheless, current lubrication models are predominantly constrained to gas–liquid two-phase scenarios, hindering the characterization of the three-phase lubrication mechanism influenced by the combined impacts of SCCO2 phase transition and ultrasonic vibration. This study formulates a lubricant film thickness model that incorporates droplet atomization, capillary permeation, shear spreading, and three-phase modulation while introducing a pseudophase enhancement factor βps(p,T) to characterize the phase fluctuation effect of CO2 in the critical region. Simulation analysis indicates that, with an ultrasonic vibration factor Af = 1200 μm·kHz, a lubricant flow rate Qf = 16 mL/h, and a pressure gradient Δptot = 6.0 × 105 Pa/m, the lubricant film thickness attains its optimal value, with Δptot having the most pronounced effect on the film thickness (normalized sensitivity S = 0.488). The model results align with the experimental trends, validating its accuracy and further elucidating the nonlinear regulation of the film-forming process by various parameters within the three-phase synergistic lubrication mechanism. This research offers theoretical backing for the enhancement of performance and the expansion of modeling in SCCO2-MQL lubrication systems.
Source: Machines
Authors: Bowen Wang, Huiping Zhang
Institution: Harbin University of Science and Technology
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,896
Award: G5604392021
OpenAlex ID: W4414406655