Year: 2025
Type: article
Abstract: The results of ab initio calculations performed for Sr2IrO4 using the density functional theory with the spin-orbit coupling and the onsite Hubbard-U correction applied to the Ir−d states are reported in order to provide more insights into known experimental data. The results demonstrate that in the stoichiometric oxide all Ir ions are in the +4 oxidation state. In the presence of an O vacancy some Ir ions turn into +3 and +2 states that is contrary to experimental observations where only the +3 state has been observed. These transitions are accompanied by the change in the magnetic moments from 0.10 μ B for Ir4+ to 0.26 μ B and 0.31 μ B for Ir3+ and Ir2+, respectively. Depending on the site where the O vacancy is formed, the change in the oxidation state leads to either the appearance of empty defect states in the gap or filled localized Ir d-states. The reasons for the absence of the Ir2+ state in experimental data are also discussed. The formation of a Sr vacancy does not cause alternation in ion oxidation states providing instead a remarkable change in the band structure of the oxide resulting in the appearance of Dirac cones at the Fermi level. No experimentally determined Ir5+ state could be detected in the presence of an Ir vacancy or an additional interstitial oxygen indicating a more complex nature of defects to provide the +5 state.
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: green
Awards: G6858549344, NAISS
OpenAlex ID: W4414588734