Correlating Structural Properties with Catalytic Stability in Nanocrystalline La(Sr)CoO3 Thin Films Grown by Pulsed Electron Deposition (PED)
Year: 2025
Type: article
Abstract: This study investigates the structural, morphological, and gas-sensing properties of pure and strontium-doped lanthanum cobaltite (La1−xSrxCoO3) perovskite thin films obtained by Pulsed Electron Deposition (PED). This sustainable ablative technique successfully produced high-quality, dense, nanocrystalline films on Si and MgO substrates, demonstrating excellent stoichiometric transfer from the source targets. A comprehensive analysis using XRD, SEM, TEM, AFM, and XPS was conducted to characterize the films. The results show that Sr-doping significantly refines the microstructure, leading to smaller crystallites and a more uniform surface topography. Gas sensing measurements, performed in a temperature range of 100–450 °C, revealed that all films exhibit a characteristic p-type semiconductor response to nitrogen dioxide (NO2). The La0.8Sr0.2CoO3 composition, in particular, demonstrated the most promising performance, with enhanced sensitivity and excellent operational stability at temperatures up to 350 °C. These findings validate that PED is a reliable and precise method for fabricating complex oxide films and confirm that Sr-doped LaCoO3 is a highly promising material for developing high-temperature NO2 gas sensors.
Source: Materials
DOI: 10.3390/ma18194550
Institution: AGH University of Krakow
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4414650793