Permanganate-fluorozirconate conversion coating as precursor for Flash-PEO on AZ31B magnesium alloy
Year: 2025
Type: article
Abstract: The corrosion resistance of AZ31B magnesium alloy was evaluated after a two-step surface treatment consisting of a permanganate–fluorozirconate conversion layer followed by Flash-PEO in a silicate–fluoride (SiF) electrolyte. Electrochemical tests after 24 hours immersion in 0.5 wt.% NaCl demonstrated that the structured coating reduced the corrosion rate when compared to the reference Flash-PEO SiF coating ((3.4 ±1.0)×10 -6 mm·yr -1 versus (1.3±0.8)×10 -5 mm·yr -1 ). After 72 hours, this trend persisted, with impedance values at low frequency one order of magnitude higher than its counterpart without precursor layer ((1.4±1.0)×10 7 Ω·cm 2 versus (2.6±1.0)×10 6 Ω·cm 2 ). Notably, Flash-PEO coatings in both cases preserved electrochemical integrity even in the presence of pre-existing surface defects. The permanganate–fluorozirconate precursor layer promoted, after Flash-PEO processing, a distinctive “coral reef-like” morphology with reduced interconnected porosity, thereby enhancing barrier properties by limiting substrate exposure to the corrosive environment. Complementary characterization confirmed the incorporation of zirconium and manganese species, along with compounds typically derived from the Flash-PEO SiF electrolyte. Chemical species 3D Models from https://next-gen.materialsproject.org/materials • Mn and Zr from the precursor layer are incorporated into Flash-PEO coating. • A “coral reef-like” morphology is induced by the precursor after Flash-PEO. • The coating morphology and the pore-sealing effect increased the corrosion resistance.
Source: Ceramics International
Institution: Universidad Complutense de Madrid
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,830
Awards: G252646220, G6666782080, G7071285012
OpenAlex ID: W4414985693