A high-temperature heat flux sensor using the transverse Seebeck effect in elemental rhenium

Year: 2025

Type: article

Abstract: Heat flux sensors compatible with hot environments are critical to advance aerospace, materials, and energy generation technologies that cope with extreme thermal conditions. In this work, we report on the development and characterization of a high-temperature heat flux sensor using the transverse Seebeck effect (TSE) in rhenium single crystals. The sensor leverages refractory alloys and ceramics compatible with temperatures exceeding 1000 °C. The heat flux sensor was characterized from room temperature to 500 °C using a temperature-controlled calibration facility. At constant temperature, the sensor’s voltage output is linear with respect to the absorbed heat flux. The responsivity of the sensor varies with increasing temperature, from 1.3 μ V/(W/cm 2 ) at room temperature to -3.2 μ V/(W/cm 2 ) at 500 °C, increasing monotonically in magnitude after changing sign from positive to negative at 300 °C. The experimental results are in good agreement with analytical predictions of the sensor’s temperature-dependent responsivity, which suggest a further increase in magnitude up to -7.4 μ V/(W/cm 2 ) at 1000 °C. These results highlight the unique characteristics of rhenium as a TSE transducer. The design offers compatibility with a wide range of operating temperatures and yields a measurement sensitivity that increases as the environmental conditions become more challenging. • A heat flux sensor for use in hot environments was developed using the transverse Seebeck effect in elemental rhenium. • The sensor is fabricated using components that are resilient to temperatures exceeding 1000 °C. • Above 300 °C, the responsivity of the sensor improves monotonically with increasing temperature. • The sensor responds to dynamic heating conditions with a time constant of 0.4 s.

Source: Sensors and Actuators Reports

DOI: 10.1016/j.snr.2025.100391

Authors: Kenneth McAfee, Peter B. Sunderland, Oded Rabin

Institution: University of Maryland, College Park

Language: English

Topic: Advanced Thermoelectric Materials and Devices

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,430

Funders: U.S. Department of Energy, National Aeronautics and Space Administration, National Energy Technology Laboratory