The action mechanism of secondary orientation on creep life in [001] oriented Ni-based single-crystal blades
Year: 2025
Type: article
Abstract: A 22% variation in creep life was found at 950°C/245 MPa in single-crystal blades with different secondary orientations. In the experimental and simulation results, it was seen that the movement of {111} <110> dislocations had caused the formation of the initial square micropores, which further led the crack to extend along the <110> orientation. The different secondary orientations had resulted in varied paths required for the crack to penetrate the specimen. At last, a model was constructed to clarify the action mechanism of the secondary orientation on creep life for single-crystal blades.
Source: Materials Research Letters
Authors: Jiarun Qin, Wenchao Yang, Shubo Cui, Chen Liu, Qiang Wang, Zhao Xin, Yanchao Zhang, Haijun Su, Lin Liu
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,459
OpenAlex ID: W4415269852