Effect of Cross- or Unidirectional Rolling on the Microstructure, Corrosion Rate, and Hemolysis of Ternary Magnesium–Zinc–Gallium Alloys
Year: 2025
Type: article
Abstract: The effect of cross- or unidirectional rolling on the microstructure, corrosion rate, texture, and hemolysis of the Mg-0.5Zn-0.25Ga and Mg-1.5Zn-0.375Ga alloys was evaluated. After both rolling processes, the microstructure of the as-cast alloys was considerably refined due to the recrystallization process, obtaining higher grain refinement after cross-rolling. The Mg-1.5Zn-0.375Ga alloy showed a finer microstructure than the Mg-0.5Zn-0.25Mg alloy due to the effect of both the severe plastic deformation obtained after cross-rolling and the higher amount of alloying elements, which act as grain refiners. After unidirectional rolling, the texture intensity of the basal plane increases, while the cross-rolled alloys show lower texture intensity due to the activation of the pyramidal and/or prismatic slip systems. The cross-rolled alloys showed a higher corrosion rate than the unidirectionally rolled alloys due to the basal texture developed. The Mg-1.5Zn-0.375Ga alloy showed a higher corrosion rate than the Mg-0.5Zn-0.25Ga alloy since the voids formed during heat treating were not fully eliminated during rolling. The Mg-0.5Zn-0.25Ga alloy after unidirectional rolling was not hemolytic (4.7%) and showed the lowest corrosion rate (0.8 mm/y). Thus, this alloy may be an excellent candidate for use in the fabrication of biodegradable implants.
Source: Metals
DOI: 10.3390/met15111165
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4415445683