Copper-Epoxy Interface Engineering for High-Frequency Chip-to-Chip Interconnects

Year: 2025

Type: article

Abstract: The reliability of high-frequency chip-to-chip (C2C) interconnects requires the durability of Cu interconnects and polymer dielectric interfaces. In this study, we examine the temperature cycling performance of Cu-epoxy interfaces, including methylimidazole and amine functional silane adhesion promoters along with electroplated or electroless metal interlayers such as Ni, NiCo 0.64 P 0.25 , NiW 0.48 P 0.10 , and CoW 0.66 P 0.17 . X-ray photoelectron spectroscopy is used to determine chemical states and compositions. O diffusion is analyzed using energy-dispersive X-ray spectroscopy. The adhesion strength was measured using a peel tester, and sheet resistance was characterized using a four-point probe before and after temperature cycle tests. Insertion losses were measured using a vector network analyzer as a function of temperature cycling. Our results indicate that organic adhesion promoters such as silanes show improvements in the initial adhesion; however, extended temperature cycling results in weakened interfaces associated with Cu oxidation. The CoW 0.66 P 0.17 metallic interlayer is more durable and exhibits a minimal 0.02 dB mm −1 change in insertion losses at 18 GHz after 1500 cycles.

Source: ECS Journal of Solid State Science and Technology

DOI: 10.1149/2162-8777/ae170a