Study on the Influence Mechanism of Particle Migration on the Stability of Weathering Crust Elution-Deposited Rare Earth Ores

Year: 2025

Type: article

Abstract: Particle migration can affect the ore bodies stability of weathering crust elution-deposited rare earth ores during leaching. It may trigger geological disasters such as landslides. Therefore, direct shear tests, microstructure characterization tests, and numerical simulation tests were adopted. The mechanical behavior characteristics of ore samples with different burial depths were explored. Simultaneously, the evolution characteristics of their microstructure, mineral composition, and failure modes were also studied. The results showed that after leaching, the cohesion (c) initially rose and then dropped as the proportion of −0.075 mm particles increased. The internal friction angle (φ) initially dropped, then increased, and finally stabilized. When its proportion was greater than 20%, the c of the middle-upper part of the ore sample was greater than that of the upper part. Meanwhile, the φ was smaller than that of the upper part. Especially when its proportion was greater than 30%, the c increased gradually with depth. XRD analysis revealed that illite and kaolinite were the main mineral components for the fine particle migration. Simulation experiment results revealed that in ore samples with 10% fine particles, there was noticeable migration and deposition in the upper part. However, it was the least in the upper middle and lower parts. Contact number and coordination number sharply decreased with depth, then increased, and finally gradually reduced. As deposition increased, the shear zone tilt angle grew larger. More secondary shear zones formed. The cracks became more evenly distributed.

Source: Minerals

DOI: 10.3390/min15111111

Authors: Ke Xiao, Zhenyue Zhang, Defeng Liu, Wenda Guo, Zhuo Chen, Ruan Chi

Institution: Wuhan Institute of Technology

Language: English

Topic: Rock Mechanics and Modeling

Subfield: Mechanics of Materials

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,896

Funder: National Natural Science Foundation of China