Role of fluorinated-component positioning in Li metal battery performance

Year: 2025

Type: article

Abstract: To boost electrochemical performance, fluorine-containing constituents are often introduced into lithium metal batteries (LMBs) to achieve superior properties. However, the underlying mechanism governing positional effects of fluorinated species remains unclear. Herein, three typical gel polymer electrolytes: fluorinated solvent-dominated (FSD), fluorinated polymer-dominated (FPD), and dual-site fluorinated-dominated (DFD) are systematically fabricated to investigate the related influence. Ionic conductivity, XPS characterization and molecular dynamics confirm the contribution of fluorinated solvent to the formation of stable and anion-derived inorganic-rich solid electrolyte interphase (SEI) layer. Density functional theory (DFT) results demonstrate that fluorinated polymer exhibits enhanced interaction energies, leading to increased free ion concentration. While Consistent conclusions can be drawn from diffusion coefficient analysis and distribution of relaxation times (DRT) results. By synergistically combining the merits of fluorinated solvents and fluorinated polymer, an ionic conductivity of 1.19 mS cm -1 is obtained for DFD and a minor polarization of 12 mV is achieved over 8000 h at 1 mA cm -1 in Li//Li battery. After assembling with LiFePO 4 , capacity retentions of 91.3% and 91.6% are maintained after 200 cycles at 1 C under 25 °C and 60 °C, showing exceptional cycling stability, respectively, particularly under elevated-temperature operating conditions. • Investigation on the mechanism governing positional effects of fluorinated species. • Fluorine incorporation in polymer segments facilitates rapid ion transport. • Fluorinated solvents facilitate the formation of an anion-derived inorganic-rich solid electrolyte interphase (SEI) layer. • A minor polarization of 12 mV is achieved over 8000 h at 1 mA cm -1 . • A high discharge specific capacity of 158.0 mAh g -1 with capacity retention of 91.6% is remained after 200 cycles at 1 C and 60 °C.

Source: Advanced Industrial and Engineering Polymer Research

DOI: 10.1016/j.aiepr.2025.10.002