Thermodynamic stability of doped ceria for solar reactors: Sublimation and surface segregation

Year: 2025

Type: article

Abstract: The stability of ceria‑based redox oxides under high‑temperature solar‑thermal operation is crucial for fuel‑producing reactors. This study demonstrates that the gas pressure governs CeO 2 sublimation from Gd 0.1 Ce 0.9 O 1.95 (GDC-10) under solar thermochemical conditions. Annealing GDC-10 at 1400 °C in vacuum (≈10 -4 bar) produces a porous, sponge like surface layer enriched in Gd, confirming selective CeO 2 sublimation; identical treatments in argon at the same temperature and duration do not generate comparable porosity. Time resolved electron microscopy reveal a diffusion controlled, linear growth of the cerium depleted zone, while dilatometry records irreversible chemical expansion, indicating structural damage. Co-doping with 5 mol % Zr (Ce 0.9 Gd 0.05 Zr 0.05 O 1.975 ) reduces CeO 2 loss and yields a saturated surface. Knudsen effusion mass spectrometry shows reduced CeO 2 volatility for the co-doped material after aging, linking thermodynamic stability to improved microstructural integrity. These results establish Zr co-doping as a potential strategy to stabilize GDC type redox oxides for durable solar thermochemical fuel production.

Source: Open Ceramics

DOI: 10.1016/j.oceram.2025.100871