Facile Synthesis of Uniform NiO Nanoparticles Exclusively Confined in Mesoporous SBA-15 with High Loading for Ammonia Decomposition

Year: 2025

Type: article

Abstract: The fabrication of highly loaded and uniformly dispersed metal oxide nanoparticles (NPs) is much desired but still remains a great challenge. Herein, the NiO NPs exclusively confined in mesoporous silica SBA-15 were obtained by using nickel nitrate hydrate as a precursor through a facile solvent-free preparation method, which comprised manual grinding of Ni(NO3)2·6H2O with SBA-15 and subsequent air calcination. Characterization results from X-ray diffraction (XRD) and transmission electron microscope (TEM) revealed that aggregation-free NiO nanoparticles with sizes of 3–5 nm were obtained at loading as high as 20 wt.% (weight%). Further increasing the NiO loading to 30 wt.% led to partial agglomeration of discrete nanoparticles to rod-like particles, while no external particles were observed. By comparing the sample derived from nickel acetate with exclusively external NiO particles, it was established that the pore confinement provided NiO nanoparticles with high thermal stability. Lastly, the catalytic performance of the prepared sample was evaluated in the model reaction of ammonia decomposition to COx-free H2, and the stable NH3 conversion of 93.7% was achieved at the weight hourly space velocity (WHSV) value of 30,000 mL·g−1·h−1 and at high temperature of 650 °C for 60 h, demonstrating the great potential of the solvent-free method in preparing thermally stable and robust supported catalysts.

Source: Catalysts

DOI: 10.3390/catal15111016