A dissimilar laser welding joint of magnesium alloys AZ80 and AM60: Microstructure analysis and mechanical behavior

Year: 2025

Type: article

Abstract: • Investigated microstructure and tensile behavior of laser-welded AZ80–AM60 joint. • Fusion zone exhibited coarse grains but maintained high work-hardening capability. • Strain localized first in the fusion zone, then shifted to AM60 during deformation. • Pores near the AM60 interface promoted microcrack nucleation and rapid fracture. This study investigates the microstructure evolution and mechanical behavior of a laser-welded dissimilar joint between wrought AZ80 and cast AM60 magnesium alloys. Microstructure analysis revealed a distinct fusion zone (FZ) spanning 1.5 mm and a heat-affected zone (HAZ) measuring 550 μm in width adjacent to the AZ80 alloy. Meanwhile, the AM60 side showed no fusion-related structural changes. The FZ microstructure had a characteristic dendritic solidification pattern, with an average grain size around 20 μm. The welded joint exhibited mechanical performance comparable to that of the base materials, with a yield strength of 137 MPa, an ultimate tensile strength of 250 MPa, and an elongation of 5.9 %. These properties resulted from precipitated phases within the FZ, strengthening the joint and the coarse-grained structure’s significant work-hardening ability. Digital image correlation (DIC) during tensile testing indicated that strain concentrated within the FZ due to its coarse microstructure. As deformation continued, the AM60 base material experienced plastic deformation, sharing the main strain burden with the FZ. In later stages, microcracks formed specifically at the FZ-AM60 interface. These microcracks coalesced, accelerating crack propagation and resulting in a main crack that caused the joint to fracture. These findings offer valuable insights into controlling failure mechanisms in dissimilar magnesium alloy welds.

Source: Journal of Magnesium and Alloys

DOI: 10.1016/j.jma.2025.10.009