Enhanced Catalytic Performance of PdOx/CuO Derived from Pd-Embedded CuBTC for Oxidative Carbonylation of Phenol

Year: 2025

Type: article

Abstract: A novel metal oxide catalyst, PdOx/CuO-ST, was prepared by calcining a Pd-embedded CuBTC precursor and compared with a PdOx/CuO-SG catalyst synthesized via a sol–gel method. Characterization results indicated that in both catalysts, Pd species were incorporated into the CuO lattice, forming synergistic interactions that lowered the reduction temperature of CuO. The PdOx/CuO-ST catalyst exhibited superior catalytic activity in the oxidative carbonylation of phenol to diphenyl carbonate when calcined at low temperature, which was attributed to well-dispersed Cu atoms and enhanced Pd–Cu integration. However, high-temperature calcination led to catalyst sintering and the formation of surface-adsorbed oxygen species, which reacted with PdO on CuO to generate inactive PdxCuyO phases, thereby reducing the active Pd2+ content and degrading catalytic performance. Under optimized reaction conditions (100 °C, 7 h, Pd/phenol molar ratio = 1/425, and 6.6 MPa), the PdOx/CuO-ST catalyst achieved a maximum phenol conversion of 79.5% and a diphenyl carbonate selectivity of 84.5%. Stability tests revealed that although the catalyst structure remained intact, deactivation occurred due to Pd leaching and the reduction in active PdO to metallic Pd0.

Source: Catalysts

DOI: 10.3390/catal15111039

Authors: Yuxin Feng, Zengjie Fu, Honglin Liu, Zhimiao Wang, Wei Xue

Institution: Hebei University of Technology

Language: English

Topic: Carbon dioxide utilization in catalysis

Subfield: Process Chemistry and Technology

Field: Chemical Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,654

Funder: National Natural Science Foundation of China