Effect of Current Density on Shear Performance and Fracture Behavior of Cu/Sn-58Bi/Cu Solder Joints

Year: 2025

Type: article

Abstract: Characterized by its low melting temperature of 138 °C, the eutectic Sn-58Bi solder expands the melting temperature range of interconnect joints in electronic packaging, making it widely used in multi-level packaging processes. However, its reliability at higher current densities poses a challenge. This paper employs a hybrid process combining laser soldering and hot-air reflow to fabricate Cu/Sn-58Bi/Cu solder joints in ball grid array (BGA) structures. Through mechanical testing under current loading, the effects of increasing current density (0 A/cm2, 0.85 × 103 A/cm2, 1.70 × 103 A/cm2, 2.55 × 103 A/cm2, 3.40 × 103 A/cm2, 4.25 × 103 A/cm2) were studied systematically. Results indicate that the shear strength decreases markedly with increasing current density, exhibiting a reduction of approximately 5.63% to 95.75%. This degradation is initiated by the overall temperature increase and material softening due to Joule heating. It is further exacerbated by the loss of the non-thermal electron wind’s strengthening contribution, which weakens as the dominant thermal impact escalates with current density. Fracture mode transitions from ductile failure within the solder matrix to a ductile-brittle mixture at the solder/IMC interface, with the transition initiating at 3.40 × 103 A/cm2. Finite element simulations reveal that current crowding in Sn-rich regions and at the solder/IMC interface induces localized Joule heating and thermomechanical strain, which jointly drive the degradation in shear strength and the shift in fracture path.

Source: Crystals

DOI: 10.3390/cryst15110945