Precipitation of Fe-25Cr-5Al-Ti-RE Ferritic Stainless Steel Under Different Quenching Temperatures
Year: 2025
Type: article
Abstract: This study investigated the variation in precipitation in Fe-25Cr-5Al-Ti-RE ferritic stainless steel under different quenching heat treatment temperatures. Quenching heat treatments were performed at five temperatures, namely 600 °C, 700 °C, 800 °C, 900 °C, and 1000 °C. To analyze the alloy’s microstructure and precipitation behavior, comprehensive characterization techniques were employed, including X-ray Diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results demonstrated that after quenching at these temperatures, the main precipitation in the alloy was a chromium-rich phase (α′), aluminum oxide (Al2O3), titanium carbide (TiC), and titanium nitride (TiN). Specifically, Al2O3 was detected exclusively after heat treatments at 800 °C, 900 °C, and 1000 °C, with its particle size ranging from 10 nm to 100 nm. During high-temperature heat treatment, aluminum atoms and oxygen atoms in the matrix interacted with each other, and fine Al2O3 particles precipitated through a solid-state phase transition. Regarding titanium-containing precipitates, TiC precipitated after heat treatments at 700 °C, 800 °C, and 900 °C, whereas TiN was only observed after the quenching treatment at 1000 °C. The size of TiC particles fell within the range of 100 nm to 400 nm, while TiN particles exhibited a significantly larger size, spanning from 5 μm to 10 μm. Thermodynamic and kinetic analyses revealed that at elevated temperatures, nitrogen (N) exhibited a relatively high diffusion coefficient in the matrix; meanwhile, titanium (Ti) demonstrated an extremely strong chemical affinity for N. Consequently, even when the N content in the alloy was at a low level, N tended to preferentially react with Ti rather than with carbon (C) to form TiN.
Source: Crystals
Authors: Xiaojian Du, Jianghua Ma, Guowang Song, Taotao Li, Jiayi Qi, Chengzhi Liu, Yucheng Yin
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,534
OpenAlex ID: W4415823660