Effect of Gd Content on the Microstructure and Mechanical Properties of Hot Extruded Mg-xGd-4Y-1Sm-0.5Zr Alloys

Year: 2025

Type: article

Abstract: In this paper, the microstructure, mechanical properties, and strengthening mechanisms of hot-extruded Mg-xGd-4Y-1Sm-0.5Zr (x = 4, 7, 10, wt.%) alloys were studied. The results show that the hot extruded alloys exhibit bimodal grain structures, and with Gd content increasing, the fraction of non-dynamic recrystallized grains gradually decreases, with 46.3%, 38.6%, and 9.3%. After aging for 200 °C × 96 h, all three hot-extruded alloys reach peak-aged hardness, and as Gd content increases, the area number density of the β′ phase increases with Gd increasing, being 7.1 × 1015/m2, 9.9 × 1015/m2, and 16.5 × 1015/m2, respectively. And the yield strength (YS) increases from 287 MPa to 345 MPa, the ultimate tensile strength (UTS) increases from 365 MPa to 418 MPa, and elongation (EL) decreases from 8.5% to 4.2%. The tensile failure mechanism is quasi-cleavage fracture. With Gd content increasing, the dimples and tear ridges on fracture surfaces gradually decrease while cleavage facets increase. The peak-aged GWS741 alloy demonstrates optimal comprehensive mechanical properties, with YS, UTS, and EL reaching 332 MPa, 409 MPa, and 7.8%, respectively. During in situ tensile testing, coarse un-DRXed grains undergo prismatic ({101-0}⟨112-0⟩) slip, while DRXed grains experience basal (0001⟨112-0⟩) slip and twinning deformation. Even at 6.6% strain, no microcracks are observed, indicating excellent plasticity. During the tensile failure process, the main crack propagates along tortuous paths, showing crack deflection characteristics, where it either penetrates through elongated deformed grains or bypasses un-DRXed grains.

Source: Materials

DOI: 10.3390/ma18215023

Authors: Lipeng Yan, Xinglin Zhu, Ranfeng Qiu, Nannan Wang, Xiaoke Zhang

Institutions: Henan Institute of Technology, Henan University of Science and Technology, Civil Aviation Flight University of China

Language: English

Topic: Magnesium Alloys: Properties and Applications

Subfield: Biomaterials

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $3,137

Funder: Henan Provincial Science and Technology Research Project