Abstract: Friction stir-based joining techniques offer a promising route for the integration of highly dissimilar materials into single structures, with potential applications in safety-critical sectors such as hydrogen storage and lightweight mobility systems. Ensuring structural integrity under dynamic loading is crucial for their industrial adoption, particularly given the strong inhomogeneity of metal–polymer interfaces. This study investigates the strain rate sensitivity of lap joints between an AA6082-T6 aluminum alloy, and a glass-fiber-reinforced polymer (Noryl™ GFN2) produced using a friction stir process. Quasi-static and intermediate strain rate (≈3 s−1) tensile tests were performed on the joints, while both base materials were additionally characterized at quasi-static, and intermediate strain rate conditions using a custom accelerated electromechanical testing device. Digital image correlation was employed to monitor deformation. The results reveal that the joints exhibit clear strain rate sensitivity, with ultimate remote stress and bending angle stiffness increasing by approximately 30% and 23%, respectively, from quasi-static to intermediate strain rate loading. Fracture consistently initiated in the polymer, indicating that the joints mechanical performance is limited by the polymeric constituent, although the polymer strain rate hardening impacts the peel/shear mix in the loading scenario of intermediate strain rate loading. Overall, the findings highlight that while friction stir metal–polymer joints benefit from strain rate hardening, their performance envelope remains governed by the polymer base material.
DOI: 10.3390/jmmp9110362
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,172
Funder: European Commission
Awards: G2542243733, G8500429480
OpenAlex ID: W4415871779