Electrochemical Urea Oxidation on Porous Ni and Ni–M (M = Ir, Pt) Electrodes Obtained via Molten-Salt Treatment Technique

Year: 2025

Type: article

Abstract: Porous Ni, Ni–Ir, and Ni–Pt electrodes were prepared on Ni substrates by molten-salt Al co-deposition followed by dealloying. SEM/EDS and XRD confirmed a Raney-type porous network with Ir or Pt present across the layer. A urea oxidation reaction (UOR) was tested in 1 M NaOH + 0.33 M urea by cyclic voltammetry and chronoamperometry at +0.40 V vs. SCE (60 min). Smooth Ni showed near-zero current. Porous Ni resulted in ~11 mA cm−2 initially and ~9 mA cm−2 after 60 min. Porous Ni–Ir started at ~7 mA cm−2 and fell to ~2 mA cm−2 within 5 min, indicating fast deactivation, likely due to Ir-oxide formation that suppresses the Ni2+/Ni3+ redox couple. Porous Ni–Pt remained at ~11 mA cm−2 over 60 min, consistent with a stable Ni–Pt effect in which Pt aids urea adsorption/activation while Ni provides the redox path for oxidation. Overall, Pt improves UOR performance, whereas Ir lowers it under these conditions.

Source: Materials

DOI: 10.3390/ma18225069

Authors: Dawid Kutyła, Michihisa Fukumoto, Hiroki Takahashi, Ryuu Takahashi, Katarzyna Skibińska, Piotr Żabiński

Institutions: AGH University of Krakow, Akita University

Language: English

Topic: Electrocatalysts for Energy Conversion

Subfield: Renewable Energy, Sustainability and the Environment

Field: Energy

Domain: Physical Sciences

SDG: Affordable and clean energy

Open Access status: gold

Estimated APC paid: $3,137