Effect of Annealing Temperature on Microstructure, Texture, and Magnetic Properties of Non-Oriented Silicon Steel for Electric Vehicle Traction Motors
Year: 2025
Type: article
Abstract: Improving the efficiency of electric vehicle traction motors requires non-oriented silicon steels with low core loss and favorable magnetic induction. This study aims to clarify the influence of annealing temperature on the microstructure, texture, and magnetic properties of a 3.2%Si–0.9%Al steel, providing guidance for process optimization. Optical metallography, X-ray diffraction, and electron backscatter diffraction were employed to characterize the evolution. Recrystallization was completed between 620 °C and 720 °C, during which fine recrystallized grains replaced the deformed structure, accompanied by the nucleation of {111}<112> and {114}<481> grains. With further annealing from 850 °C to 1050 °C, grain growth occurred, resulting in an α*-fiber texture dominated by {114}<481>. The fraction of high-angle {114}<481> grains increased, while low-angle {111}<112> grains decreased. This microstructural evolution significantly influenced the magnetic properties of non-oriented electrical steel. The P1.5/50 and P1.0/400 core losses reached minimum values of 2.02 W/kg and 16.48 W/kg at 1010 °C and 930 °C, respectively, while B50 decreased slightly from 1.670 T to 1.652 T. These findings indicate that precise control of the annealing temperature is an effective strategy to tailor microstructure and texture, thereby optimizing the magnetic properties of non-oriented electrical steel.
Source: Metals
DOI: 10.3390/met15111235
Authors: Shaoyang Chu, Li Xiang, Feihu Guo, Shengtao Qiu
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
Award: G28956904
OpenAlex ID: W4416067743