The Influence of Initial Microstructure on the Microstructure and Mechanical Properties of Ductile Iron After Nanostructurisation Heat Treatment
Year: 2025
Type: article
Abstract: In this study, the microstructure and mechanical properties of ductile cast iron subjected to a novel austempering treatment were investigated. The methodology was based on prolonged isothermal annealing within the low-temperature range of the bainitic transformation. The experiments were carried out on samples with two different initial microstructures: pearlitic-ferritic and ausferritic. Two long-term austempering treatment variants were designed and tested: single (AT-1) and double (AT-2). In both cases, the heat treatment led to the production of a nanoausferritic microstructure, characterized by exceptionally thin plates of bainitic ferrite separated by thin layers of retained austenite. Compared to conventional austempering, the new method produced a much finer microstructure and a reduced amount of retained austenite. Moreover, the AT-2 variant further enhanced the homogeneity of the microstructure, promoting a higher fraction of thin ferrite plates. Mechanical tests revealed that the new heat treatment significantly improved the performance parameters of the material: hardness increased from 27 HRC to 32-35 HRC, tensile strength rose from 1027 MPa to 1220-1296 MPa, and yield strength from 683 MPa to 1033-1054 MPa. It was proved that, regardless of the initial microstructure of ADI, new processes exhibited comparable, enhanced mechanical properties, confirming their efficiency and universality.
Source: Nanomaterials
DOI: 10.3390/nano15221710
Authors: Emilia Skołek, Paweł Skoczylas, Kamil Wasiluk, Wiesław A. Świątnicki, Andrzej N. Wieczorek, Dawid Myszka
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,896
Funder: Narodowe Centrum Badań i Rozwoju
Awards: G1843972583, G3024639123, G985590090
OpenAlex ID: W4416138216