Optimisation of Sunflower Husk Ash-Activated Slag Binder

Year: 2025

Type: article

Abstract: This study presents the optimisation of an alkali-activated binder produced from ground granulated blast furnace slag (GGBFS) and potassium-rich sunflower husk ash (SHA), by varying SHA content, curing regime, and mixing procedure. Both materials are locally available in the Republic of Serbia. The influence of SHA content (15%, 25%, and 35% by mass of GGBFS) and curing conditions (ambient and 65 °C) on hydration products, workability, and compressive strength was examined. The water-to-binder ratio and GGBFS content were kept constant, and a one-part alkali activation approach was employed using untreated SHA. Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA) were performed on paste samples, after 2, 7 and 28 days of curing, while workability and compressive strength of mortars were measured after 7 and 28 days. Increasing SHA content enhanced the formation of C-S-H and C-A-S-H gels, resulting in a consistent rise in compressive strength, from 26.6 MPa to 36.2 MPa after 7 days and from 46.2 MPa to 55.1 MPa after 28 days of ambient curing. Workability was slightly reduced with increasing SHA content, resulting in flow diameters of 156.04 mm (15% SHA), 154.10 mm (25% SHA) and 152.76 mm (35% SHA). Curing at 65 °C accelerated early strength gain for 33% to 39% but produced lower 28-day strengths than ambient curing. Additionally, for the optimal mix, SHA was also pre-immersed in water for varying durations to assess its effect on workability, compressive strength, and potassium ion leaching. This pretreatment increased compressive strength by up to 14.7%, depending on immersion time, but reduced workability by up to 15.5%. The novelty of the research is reflected in attaining the highest 28-day compressive strength of 55 MPa (for 25% SHA by mass of GGBFS), under ambient curing, without SHA pretreatment or immersion, highlighting the potential for low-energy, sustainable binder systems using agricultural and industrial by-products.

Source: Buildings

DOI: 10.3390/buildings15234210

Authors: Olivera Bedov, Suzana Draganić, Snežana Vučetić, Marijana Serdar

Institutions: University of Novi Sad, University of Zagreb

Language: English

Topic: Concrete and Cement Materials Research

Subfield: Civil and Structural Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,137