Abstract: Non-oriented (NO) Fe–Si electrical steels are key materials for magnetic cores of electrical machines, requiring a balance between magnetic and mechanical properties. This study systematically examined the effect of silicon content (1.06 wt%, 2.15 wt%, and 3.09 wt%) on the microstructure, mechanical, and tribological behavior of three produced NO steel grades. Mechanical properties were assessed using tensile tests, microhardness, and nanoindentation, while tribological performance was evaluated under dry reciprocating sliding (ball-on-flat) against a 100Cr6 steel ball at loads of 5 N, 10 N, and 25 N. Increasing silicon content led to larger grain size, higher hardness (227 HV–361 HV) and strength, but lower ductility. Tribological behavior depended on both composition and load. The most stable friction regime occurred at 10 N. The medium-Si steel (N3, 2.15 wt%) exhibited the best performance with a low coefficient of friction (COF ≈ 0.52–0.55); N5 (3.09 wt%) showed a similar COF, while N1 (1.06 wt%) had a slightly higher value. At 25 N, an inverse relationship between hardness and friction appeared: softer N1 had the lowest COF (≈0.68–0.70), whereas harder N3 and N5 reached ≈ 0.74–0.78. Scanning electron microscopy (SEM) observations revealed abrasive wear for N3/N5 and plastic flow (galling) for N1. Overall, an optimal silicon content provides the best compromise between hardness and tribological stability depending on load conditions.
Source: Crystals
Authors: Marcela Motýľová, Ivan Petrišinec, Róbert Džunda, Jana Andrejovská
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,534
OpenAlex ID: W4416601000