Fabrication and performance analysis of a photocatalytic self-cleaning superhydrophobic coating for cement-based exterior wall materials
Year: 2025
Type: article
Abstract: To address the issues of low photocatalytic efficiency and poor hydrophobic durability of traditional coatings. A photocatalytic self-cleaning superhydrophobic coating was prepared by compounding anatase TiO2 with silane reagents and SiO2, and using the sol-gel method combined with a hydrothermal synthesis process. Performance tests show that the photocatalytic degradation efficiency of this coating reaches 96.7%, the contact Angle is maintained above 140°, the mass loss is only 0.5% after 28 days of acid and alkali erosion, the composition contents of O, Si, Ti and C elements are 51.2%, 21.6%, 16.4% and 10.2% respectively, and the pore size is 10.1 nm. The specific surface area is 16.4 m2 /g. This coating, through the coupling of photocatalysis and superhydrophobic properties, achieves the optimization of long-term self-cleaning, corrosion resistance, anti-aging and durability of building exterior wall materials.
Authors: Hao Li, Xiaokang Zhang, Zhengdong Yu, Yingfeng Hu
Language: English
Subfield: Surfaces, Coatings and Films
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,060
OpenAlex ID: W4416893039