Tuning the properties of erbium oxide through manganese doping for enhanced optoelectronic performance

Year: 2025

Type: article

Abstract: Researchers are increasingly drawn to erbium oxide (Er 2 O 3 ) nanoparticles because of their attractive properties, which include luminescence, high electron mobility, optical band gap, and exceptional transparency. These qualities make them a potential choice for a range of optoelectronic applications. Using the solid-state reaction technique, it is possible to produce erbium oxide nanoparticles, both undoped and doped with 1–5% manganese (Mn). This investigation compares undoped and Mn-doped Er 2 O 3 nanoparticles with respect to their optical, electrical, and magnetic properties. The X-ray diffraction pattern shows that the Er 2 O 3 nanoparticles made with 5% Mn doping have a cubic crystal structure, the biggest crystallite size (60.90 nm), and less microstrain. The FTIR spectrum shows peaks at 417 cm −1 and 433 cm −1 for the Er-O stretching vibrations and at 461 cm −1 and 500 cm −1 for the Mn–O bond. The direct energy band gap for Er 2 O 3 nanoparticles that are doped with 0–5% manganese content is confirmed by UV visible examination. As a consequence of electron–hole pair recombination, photoluminescence (PL) spectra show several emission peaks in the visible spectrum. According to the Raman investigation, the insertion of manganese into Er 2 O 3 maintains the cubic phase while causing a modest modification to the local bonding conditions. This is demonstrated by the fact that the T g and E g vibrational modes remain stable. At 5% Mn doping, the magnetic study of Er 2 O 3 nanoparticles reveals the maximum saturation magnetization of 2.686 emu/g. The highest conductivity of Er 2 O 3 nanoparticles is observed at a doping level of 5%, while the lowest conductivity is observed at a doping level of 2%, according to electrical properties. Furthermore, it has been discovered that the work function for erbium oxide nanoparticles doped with 0 to 5 percent manganese is between 5.375 and 5.56 electron volts. The results of the study indicate that by eliminating surface imperfections, minor Mn doping in Er 2 O 3 improves stability and raises the work function. However, greater Mn concentrations cause more defects, which may impair work function by donating electrons. This study shows that controlled Mn doping in Er 2 O 3 nanoparticles tunes their band gap, enhances photoluminescence, and induces ferromagnetism, demonstrating their multifunctionality for optoelectronic devices. In light of all of these considerations, Mn-doped Er 2 O 3 nanoparticles show considerable potential as a material for a range of optoelectronic applications.

Source: Journal of Materials Science Materials in Electronics

DOI: 10.1007/s10854-025-16188-7