Phase-Driven Property Modulation in BiVO 4 Ceramics via Multi-ion Substitution for Next-Generation Wireless Communication
Year: 2025
Type: article
Abstract: High Resolution Image Download MS PowerPoint Slide The growing demand for faster and more reliable wireless communication has increased the need for microwave dielectric ceramics with high performance and thermal stability. In this paper, we synthesized Bi 1–4 x (La x Nd x Sm x Eu x )VO 4 ceramics (0.025 ≤ x ≤ 0.1) via a conventional solid-state method at a low firing temperature range of 740–860 °C. Structural analysis was conducted using X-ray diffraction, high-resolution transmission eleectron microscopy, and Raman spectroscopy and showed a composition-driven phase transition from monoclinic scheelite (space group: I 2/ a ) to tetragonal zircon (space group: I 41/ amd ) near x ≈ 0.075, with a mixed-phase region observed at relatively lower substitution levels. This structural change had a direct influence on the dielectric properties: the permittivity (ε r ) decreased from 66.98 at x = 0.025 to 19.85 at x = 0.1, while the quality factor ( Q f ) increased from 7904 to 16240 GHz. A nearly temperature-stable point was identified at x = 0.055, where τ f reached +8.42 ppm/°C, which is attributed to a compensation effect arising from A-site cation rattling. Far-infrared analysis confirmed that phonon absorptions dominate the dielectric response in the microwave region. To validate practical applicability, a microstrip patch antenna fabricated from the x = 0.055 ceramic achieved a return loss of −22.5 dB at 2.46 GHz, along with 98.8% radiation efficiency and a peak gain of 5.22 dB. These results highlight that controlling the multi-ion substitution and their ratios provides an effective strategy for tuning the phase composition and dielectric performance in BiVO 4 -based ceramics, which has a strong potential for ISM-band communication devices and emerging wireless technologies.
Authors: Chunchun Li, Guobin Zhu, Deqin Chen, Jibran Khaliq
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,500
OpenAlex ID: W4416947170