A HF-Free Synthesis Method for High-Luminescent Efficiency Narrow-Bandgap Red Phosphor K3AlF6: Mn4+ with NH4HF2 as the Molten Salt

Year: 2025

Type: article

Abstract: Mn4+-doped fluoride red phosphors are widely used in white LED lighting and display applications due to their excellent luminescent properties. However, their synthesis relies heavily on highly toxic aqueous hydrofluoric acid, which not only causes severe environmental and soil/water pollution but also makes it difficult to control the microstructure of the products due to the rapid reaction rate. In this study, low-melting-point NH4HF2 was used as the molten salt, with KMnO4 and MnF2 as manganese sources, to synthesize the red phosphor K3AlF6: Mn4+ via the molten salt method. After the reaction, impurities such as NH4HF2 were removed by washing with a dilute H2O2 solution. The microstructure, photoluminescence properties, thermal quenching behavior, and application in warm white light-emitting diodes (W-LEDs) of the K3AlF6: Mn4+ phosphors were investigated. The results indicate that the phosphors prepared by this method consist of a single pure phase. By adjusting the molten salt content, the morphology of the product can be transformed from nanoparticle-like to nanorod-like structures. All products exhibit the characteristic red emission of Mn4+ under blue and violet light excitation, with the optimally doped sample achieving an internal quantum efficiency (IQE) of 69% under blue light excitation. The combination of the obtained K3AlF6: Mn4+ with the yellow phosphor YAG enabled the fabrication of W-LEDs. These W-LEDs achieved a color rendering index (Ra) of 86.8, a luminous efficacy (LE) of 77 lm/W, and a correlated color temperature (CCT) of 3690 K, along with excellent color stability under operating conditions.

Source: Solids

DOI: 10.3390/solids6040066

Authors: Chenxing Liao, Feng Zhou, Wei Xie, Liaolin Zhang

Institutions: Jiangxi University of Science and Technology, Lingnan Normal University

Language: English

Topic: Luminescence Properties of Advanced Materials

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $1,207

Funders: National Natural Science Foundation of China, Natural Science Foundation of Jiangxi Province