Comprehensive Investigations on the Effects of Heat on “Illite–Zeolites–Geo-Polymers–Sand” Composites: Evolutions of Crystalline Structures, Elemental Distributions and Si/Al Environments

Year: 2025

Type: article

Abstract: This research constitutes a novel experimental approach to valorizing an industrial by-product: the ‘brick’. Studies put emphasis on the importance of detailed structural characterization of brickminerals and their chemical evolution upon heating, contributing rationally to the design and development of new glass–ceramic forms that would be suitable for efficiently encapsulating radio-nuclides. The brick used is a complex material composed of metakaolinite, illite, sand and impurities such as rutile and iron oxides/hydroxides. Raw brick was first activated with a range of sodium hydroxide concentrations, and, second, cured at different temperatures from 90 °C to 1200 °C. Alkali-brick frameworks gradually decomposed during the firing, and turned into crystalline ceramic phases (analcime and leucite) embedded inside an amorphous silica-rich phase. After each heating stage, the cured-brick sample was exhaustively characterized by using a variety of advanced analytical techniques, including powder X-ray diffraction, ESEM/EDS microscopy and 29Si-27Al-MAS-NMR spectroscopy. Ultra-high magnetic field NMR (28.2 T) was used to distinguish and quantify Al(IV), Al(V) and Al(VI) configurations, and to better follow distinctive changes in 27Al environments of brickminerals under thermal effects. Glass-ceramized brick exhibited high specific density (~2.6 g·cm−3), high compactness and good corrosion resistance under static, mild and aggressive conditions, attesting to its high solidification and chemical durability.

Source: Ceramics

DOI: 10.3390/ceramics8040149

Authors: Abdel Boughriet, Grégory Tricot, Bertrand Revel, Viviane Bout-Roumazeilles, Sandra Ventalon, Michel Wartel