Ablation behavior of Hf-Zr-modified silicon-based ceramic coatings prepared by polymer derived ceramics and gaseous silicon infiltration

Year: 2025

Type: article

Abstract: To improve the ablation resistance of C/C composite at temperatures exceeding 2000 °C, a (Hf-Zr)C-SiC Ultra-High Temperature Ceramic (UHTC) coating was prepared by Polymer Derived Ceramics (PDCs) and Gaseous Silicon Infiltration (GSI). The linear ablation rate of the coated C/C composites was as low as 0.27 μm/s, maintaining a level as low as 10 -4 mm/s. This low R l is attributed to the formation of a well-bonded double-layered oxide scale with high thermal stability, consisting of an exterior SiO 2 glass layer and an interior Hf-Zr-Si-O complex oxide layer. Meanwhile, the dissipation of the residual Si and the C phase relieves heat accumulation, ensuring that the recorded surface temperature remains below 2000 °C, thereby enhancing the ablation resistance. Additionally, a cyclic evolution of linear ablation rate was found, due to the alternating dominant role of oxidation and mechanical denudation on the coating during ablation. This study provides theoretical and experimental support for the long-term anti-ablation design of highly dense UHTC coatings.

Source: Chinese Journal of Aeronautics

DOI: 10.1016/j.cja.2025.104010