Study on Calcified Alkali Leaching of Vanadium-Extracted Tailings and Preparation of Barium Orthovanadate

Year: 2025

Type: article

Abstract: While vanadium-extracted tailings contain valuable components, their utilization is difficult due to their high sodium content. In this work, a new oxygen-pressure calcification and alkaline leaching strategy to achieve barium orthovanadate vanadium precipitation is developed to realize the resourceful recycling and utilization of vanadium-extracted tailings. First, the preparation of barium orthovanadate via calcified alkaline leaching and vanadium precipitation was studied, and the effects of CaO addition, NaOH concentration, leaching temperature, and liquid-solid ratio on the leaching rates of sodium and vanadium were evaluated in single-factor experiments. Under the optimum leaching conditions (CaO addition of 20%, alkali concentration of 150 g·L⁻¹, leaching temperature of 180 °C, and liquid-solid ratio of 10:1), the leaching rates of vanadium and sodium reached 85.25% and 82.36%, respectively. Subsequently, the vanadium-containing leaching solution was subjected to a vanadium precipitation test, and the effects of pH, Ba(OH)₂ addition (expressed as nBa/nV), vanadium precipitation temperature, and vanadium precipitation time on the vanadium precipitation rate were investigated. Under the optimum vanadium precipitation conditions (pH 14, nBa/nV = 1.5:1, temperature of 30°C, reaction time of 60 min), a vanadium precipitation rate of more than 99% was achieved. The precipitated vanadium product of this reaction was confirmed to be Ba3(VO4)2 with a purity of more than 99%. Notably, the wastewater generated during the test process can be mixed with an alkali and returned to the leaching process for reuse, and the dealkalized residue can be used as a raw material for ore reduction in iron smelting processes.

Source: Nanomaterials

DOI: 10.3390/nano15241889

Authors: Jinwei Qu, Tingan Zhang, Xinyu Hao, Na Ma, Zhihe Dou, Ting'an Zhang

Institutions: Hezhou University, Wuhan University of Science and Technology, Northeastern University, Guilin University of Technology

Language: English

Topic: Metal Extraction and Bioleaching

Subfield: Biomedical Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Clean water and sanitation

Open Access status: gold

Estimated APC paid: $2,896