(Ca/Zn)CO 3 Microparticles Loaded with Bacitracin─Antibacterial and Osteogenic Dual Action Carriers

Year: 2025

Type: article

Abstract: High Resolution Image Download MS PowerPoint Slide Calcium carbonate (CaCO 3 ) microparticles are widely used in biomedical engineering, mainly in the field of bone tissue regeneration. This study aimed at the development of CaCO 3 -based carriers for an antimicrobial peptide, bacitracin (BCT), with antibacterial and osteogenic properties. The first part of the study was devoted to CaCO 3 microparticles obtained by the precipitation method from equimolar Na 2 CO 3 and CaCl 2 solutions. The morphology, size, and surface area of the microparticles were strongly dependent on the parameters used during the reaction (i.e., the mixing speed and geometry of the container). However, BCT adsorption on CaCO 3 microparticles was insufficient (maximum drug loading of approximately 1%); therefore, the microparticles were enriched with Zn 2+ ions (5%, 10%, or 20% vol. of the CaCl 2 solution used for precipitation was exchanged to equimolar ZnCl 2 solution). This innovative approach significantly influenced the properties and BCT adsorption capacity of the microparticles. The microparticles containing Zn 2+ were larger and cubic in shape with a predominant calcite structure. The adsorption efficacy of BCT increased significantly (maximum drug loading of approximately 40%) due to the strong affinity of BCT to Zn 2+ . BCT was released from the microparticles within 24 h, and the degradation of Zn 2+ containing microparticles was three times slower than in the case of nonmodified CaCO 3 microparticles. The microparticles were cytocompatible with L929 fibroblasts and human mesenchymal stem cells (hMSCs), except for the microparticles with the highest Zn 2+ content. The microparticles with adsorbed BCT successfully inhibited the growth of Staphylococcus aureus, Staphylococcus epidermidis, and Streptococcus pyogenes . (Ca/Zn)CO 3 microparticles enhanced osteogenic differentiation of hMSCs; however, this effect should be attributed to the release of Zn 2+ rather than BCT. The newly developed (Ca/Zn)CO 3 microparticles with adsorbed BCT could in the future serve as antibacterial and osteogenic materials for the treatment of bacterial infections and regeneration of bone tissue.

Source: ACS Omega

DOI: 10.1021/acsomega.5c06594

Authors: Katarzyna Reczyńska-Kolman, Kamil Kornaus, Dorota Ochońska, Monika Brzychczy-Włoch, Elżbieta Pamuła

Institutions: AGH University of Krakow, Jagiellonian University

Language: English

Topic: Bone Tissue Engineering Materials

Subfield: Biomedical Engineering

Field: Engineering

Domain: Physical Sciences

SDG: Good health and well-being

Open Access status: gold

Estimated APC paid: $1,935