Systematic Study on the Role of Mn, Si, and Fe on the Corrosion Resistance of Ni-Based Superalloys Exposed to Air, Gaseous Sulfur Oxides and Salts
Year: 2025
Type: article
Abstract: This work investigates the effect of alloying elements Mn, Si, and Fe on the corrosion resistance of polycrystalline Ni-based superalloys, at $$700\,^{\circ }{\hbox {C}}$$ 700 ∘ C in air and 300 vpm $${\hbox {SO}}_{2}$$ SO 2 under 5 $${\mu {\hbox {g}}}\,{{\textrm{cm}}^{2}\,h}$$ μ g cm 2 h salt coating. Oxide scale morphology and composition was investigated using SEM–EDX and APT, revealing Mn–Fe-enriched $${\hbox {Co}}_{3}{\hbox {O}}_{4}$$ Co 3 O 4 particles in the upper outward growing scale as well as Si-Fe-enriched clusters in NiO. Along the NiO– $$ {\hbox {Co}}_{3}{\hbox {O}}_{4} $$ Co 3 O 4 phase boundary, a tight network of Fe-decorated dislocations relieving stress between the lattices was identified through APT. In the inward growing scale, Si enrichment was observed in the form of oxides and sulfides, while no Mn was detected. Graphical Abstract
Authors: Cynthia Rodenkirchen, Victoria Minns, Adriana Encinas-Oropesa, John Nicholls, Mark Hardy, Stella Pedrazzini
Language: English
Subfield: Aerospace Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,990
OpenAlex ID: W4417510384