Design and preparation of a three-dimensional interface structure Al/Mg laminated composites

Year: 2025

Type: article

Abstract: • The Al/Mg LMCs with a 3D interface structure were prepared through wood-like mortise-tenon joints interface structure design. • The interfacial shear strength of Al/Mg LMCs with a 3D interface structure was higher than 40 MPa. • The 3D interface structure can significantly improve the interfacial bonding strength and plasticity of Al/Mg LMCs. To solve the problems of low interlayer bonding strength in Al/Mg Laminated metal composites (LMCs). This work took advantage of the fact that the three-dimensional (3D) interface structure can increase the interface contact area, hinder crack propagation, and delay interface cracking, and proposed to use spark plasma sintering (SPS) to prepare Al/Mg LMCs with 3D interface structure. The influence of the sintering temperature on the interface microstructure and mechanical properties of 2A12-Al/AZ91-Mg LMCs was systematically studied. The results indicate that 2A12-Al/AZ91-Mg LMCs with 3D interface structure similar to wave shape or gear meshing shape can be obtained by SPS integrated sintering. When the SPS integrated sintering temperature increased from 420 °C to 440 °C, a typical three-layer diffusion layer was formed at the 2A12-Al/AZ91-Mg interface. Moreover, the diffusion layer gradually transformed from a solid-phase diffusion characteristic to a solid–liquid coexistence diffusion characteristic. Meanwhile, the interface shear strength at 430 °C was the largest, which was 49.4 ± 2.67 MPa. The high interfacial shear strength benefits from the hindrance and suppression of cracks by this 3D interface structure.

Source: Materials & Design

DOI: 10.1016/j.matdes.2025.114403