Operando FTIR investigation of salt dynamics in Li-ion batteries during fast charging

Year: 2025

Type: article

Abstract: Li-ion batteries, when charged at fast-charging rates ( > 2C), suffer from reduced lifetimes and can undergo catastrophic failure. During high-rate charging, Li-ions are unable to rapidly transport through high-loading electrodes ( > 4 mAh cm −2 ). This results in unequal charge distributions, potentials, and utilization of the active material, which can lead to Li plating. Li-ion concentration polarization, in which Li-ions deplete in the anode and accumulate in the cathode during charging, precedes Li plating. An operando FTIR-ATR graphite/NMC cell developed in this research captured Li-ion concentration polarization in real-time. During fast charging, decreases in Li-ion concentration ( > 95%) were measured at the back of the anode. This is the first verification of complete Li-ion depletion within the anode at high C-rates. The measurements also showed graphite stage transition. A P2D model was developed for comparison to the operando measurements. The measurements agreed with the model in some cases, but disparities existed at high C-rates and loadings. In the experiment, the Li-ion concentration often failed to recover to 1.2 M until several hours after charging, whereas the model Li-ion concentration rapidly recovered. The contrast between the model and experiment results indicates that further investigation is required to improve understanding of Li-ion concentration dynamics during fast charging. • An operando FTIR Li-ion battery enables real-time Li-ion concentration measurements. • A P2D model and FTIR measurements show large Li-ion decreases during charging. • FTIR measurements reveal graphite phase change and agree with a P2D model. • Experimental measurements indicate fast-charging recovery may be slower than predicted.

Source: Journal of Power Sources

DOI: 10.1016/j.jpowsour.2025.238058