Formation of Mn4Si7 thin films by solid-phase ion-plasma method and improvement of their thermoelectric and electrophysical properties
Year: 2025
Type: article
Abstract: • In this work, a thin coating of Mn 4 Si 7 of was formed substrates using magnetron sputtering. • It was found that the band gap of the silicide is Eg = 0.66 eV. • It was found that the nanocrystallites with dimensions in the range of 50–100 nm. In this study, Mn 4 Si 7 thermoelectric thin films were deposited on Si(111) and SiO 2 /Si(111) substrates via magnetron sputtering, and their microstructural as well as electrical temperature-dependent properties were thoroughly investigated. The as-deposited films at room temperature exhibited an amorphous structure, which underwent a phase transition to a polycrystalline state upon annealing at 800 K. This annealing process resulted in a significant reduction of surface defects and the formation of a continuous film composed of nanocrystallites with dimensions in the range of 50–100 nm. The presence of the SiO 2 dielectric layer on the substrate induced distinct variations in the film’s microstructure and density, which in turn affected its electrical resistivity and thermoelectric performance. The enhancement of thermoelectric properties observed during the amorphous-to-crystalline phase transition is attributed to the selective scattering mechanism of charge carriers at nanocluster boundaries. These findings provide a critical foundation for achieving high-performance Mn 4 Si 7 -based thermoelectric thin films and expand their potential applications in thermoelectric devices, paving the way for the development of next-generation energy conversion materials.
Source: Materials Letters X
Authors: M.T. Normuradov, I.R. Bekpulatov, V.V. Klechkovskaya, Kim Ki Buem, B.D. Igamov, M.S. Lukasov, Gunel Imanova, E.A. Kerimov, Sh.A. Zeynalov
Institutions: Karshi State University, Federal Scientific Research Centre Crystallography and Photonics, Sejong University, Academy of Sciences Republic of Uzbekistan, Russian Academy of Sciences, A.V. Shubnikov Institute of Crystallography, Khazar University, Western Caspian University, Azerbaijan State University of Economics, Ministry of Science and Education Republic of Azerbaijan, Radiasiya Problemləri İnstitutu, Azerbaijan Technical University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,240
OpenAlex ID: W7077076105