Drying shrinkage and moisture loss of lightweight concrete mixed with fine recycled concrete aggregate (FRCA)
Year: 2025
Type: article
Abstract: The paper reports on drying shrinkage and moisture loss of lightweight concrete exposed to the natural laboratory environment. Concrete was designed using fine recycled concrete aggregate, sand, cement, silica fume, foaming agent and water. Four mixed designs were utilized. The quantity of silica fume used to replace cement was about 10% (by weight of cement). Meanwhile, fine recycled concrete aggregate (FRCA) was used to replace sand from 0% to 30% by weight of sand. Three specimens (300mm x 75mm x 75mm) were cast for each mix and cured for one day. Specimens were measured for shrinkage and moisture loss. The duration of the test was 28 days. Findings from this study show that all the lightweight foam concrete used in this study shrinks in a fluctuating trend when exposed to a natural laboratory environment. The concrete mixed with 20% and 30% of FRCA had the highest and lowest shrinkage values at 28 days, respectively. For every concrete mix, the trend of moisture loss is quite consistent. The concrete with 20% FRCA experienced the largest percentage of moisture loss, which supports the cause of the highest shrinkage strain. Conversely, concrete containing 30% FRCA exhibits the best link between drying shrinkage and moisture loss.
Authors: Norisham Ibrahim, Izzah Inshirah Rasli, SD Guthrie Tower, 2, Jalan PJU 1A/7, Ara Damansara, 47301 Petaling Jaya, Selangor, Malaysia, Mohd Afiq Mohd Fauzi, Zubaidah Sulong, Engineering and Environmental Consultants Sdn. Bhd, Taman Tun Dr. Ismail, 60000, Kuala Lumpur
Language: English
Subfield: Building and Construction
Field: Engineering
Domain: Physical Sciences
Open Access status: bronze
OpenAlex ID: W7081931801
FWCI:
Cites:
Cited by:
Related to: